ALD-2103 is a crystal-clear, low-viscosity epoxy resin and is produced and distributed exclusively in premium quality. ALD-2103 is ideal for almost any application. For example: in the jewelery sector, table manufacturing, for river tables for floors, ponds,aquarium and terrarium construction, as well as for boat, ship and aircraft construction.
| Item (ALD-2103) |
Epoxy Resin(A ) |
Hardener(b ) |
| Color |
clear |
clear |
| Viscosity@25ºC(mpa.s) |
380-450 |
30-40 |
| Mix Ratio(by weight) |
2 |
1 |
| Hardness(Shored) |
75-80 |
| Operation time(100g mixed glue ,25ºC) |
50-60minutes |
| Curing Time(25ºC) |
24-26hours |
| Curing Time(35ºC) |
8hours |
Product Advantage
* Non-toxic
* 100% Solid
* VOc Free
* Solvent Free
* Crystal Clear
* Epoxy Resin and hardener,mix ratio of 2:1
* Thick Pour to 2"-4"
1. Mirror-Like Crystal Clear Finish
The Highest super wet with gloss finish with unparalleled depth and clarity that is formulated to use within all coating and step casting applications
2. High-Grade UV Resistance
All epoxies will turn yellow overtime. What makes our Super clear Epoxy resin crystal clear kit different is our specific high-grade additive formulation. Ours will yellow less and remain ultra-crystal-clear over a longer period of time than any of our competitors. Our products are made for you, and made to last, bar none.
3. Integrate Color With Ease
Perfectly suited for accepting and dispersing mica powder pigments, liquid pigments paste and alcohol inks and dyes.It is the ideal epoxy for evenly distributing color and suspending inks and powders. Paint, acrylic paint and oil based paint are not recommended to use with epoxy, and can have negative results.
4. Integrate Color With Ease
Perfectly suited for accepting and dispersing mica powder pigments, liquid pigments paste and alcohol inks and dyes.It is the ideal epoxy for evenly distributing color and suspending inks and powders. Paint, acrylic paint and oil based paint are not recommended to use with epoxy, and can have negative results.
5.Advanced Formula for StrengtWith tables, table tops and countertops you need durability.That's why we crafted an epoxy formulation with an 80+ Shore D Strength Rating when fully cured
Application
How to use
Package and Shipment
Company
FAQ
1.Q: What's the best way to mix this?
A: You'll want to make sure that you have 2 parts base resin and 1 part curing agent measured precisely, by volume. Pour each into your mixing bucket, and we recommend mixing by hand for at least 3 minutes and between 3-5 minutes or until it is fully mixed. Be careful to scrape the
sides while mixing, but when pouring, do not scrape the sides. This can impart unmixed material that may cling to the side and has not been incorporated. Don't worry about any bubbles in the mixture, they will all work themselves out.
2.Q: How long does it take to cure, and what temperatures can I pourthis in?
A: Our optimum environment temperature range is 72° - 84°F (in a clean, temperature controlled environment. In that temperature range, it will begin to gel in 20-30 minutes, and cure rock hard within 24 hours.Temperatures under 70° will slow the curing process even more, and the closer you get to 60° the curing process will stop. Above 85°, it will begin to accelerate curing, leading to cracking, shrinking and other negative results.
3.Q: Is your epoxy FDA Compliant?
A: The short answer is, yes. Once our epoxy has cured, it becomes safe,per FDA code, 21CFR175.300 which states "Resinous and polymeric coatings may be safely used as the food-contact surface of articlesintended for use in producing, manufacturing, packing, processing,
preparing, treating, packaging, transporting, or holding food" and can be used as a "functional barrier between the food and the substrate".
4.When Can I Demould?
A: Our optimum environment temperature range is 72° - 84°F in a clean temperature controlled environment. In that temperature range, you can demould between 18 and 24 hours, and its optimal workability will be at 24-30 hours. At 30 hours it will sand and plane as easy as wood!
){kind=link}